Change search
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf
Inferring the development of microsegregation and microstructure in Spheroidal and Compacted Graphite Iron using EPMA‐WDS
Jönköping University, School of Engineering, JTH, Materials and Manufacturing.ORCID iD: 0000-0001-6938-037X
Jönköping University, School of Engineering, JTH, Materials and Manufacturing.ORCID iD: 0000-0002-3024-9005
2017 (English)In: Solidification Processing 2017: Proceedings of the 6th Decennial International Conference on Solidification Processing / [ed] Zhongyun Fan, Brunel Centre for Advanced Solidification Technology (BCAST) , 2017, no 1, p. 455-458Conference paper, Published paper (Refereed)
Abstract [en]

Microsegregation is closely related to the solidification characteristics and microstructure development of a material. In this paper, the microsegregation of Si, Cu, Mn, and P was investigated on a spheroidal and a compacted graphite iron using a modified EPMA equipped with WDS spectrometers. On the basis of the approximated local equilibrium eutectic temperature, the solidification sequence of the matrix was estimated. The inferred microstructure development appeared to correspond well to published interrupted solidification experimental results. Solute profiles and effective partition coefficients were constructed using the solidification sequence. While the spatial microsegregation patterns clearly differed between the two materials, solute profiles and effective partition coefficients were very similar. For Si, Cu and Mn, the solute profiles corresponded reasonably with simulation results produced using the Scheil-Gulliver module of the Thermo-Calc software with the TCFE7 databank, indicating back-diffusion of these elements is negligible for SGI and CGI with solidification times up to 10 min. The effective partition coefficients for Si, Cu and Mn were fairly constant until about 90% of the matrix had solidified, after which they appeared to approach unity.

Place, publisher, year, edition, pages
Brunel Centre for Advanced Solidification Technology (BCAST) , 2017. no 1, p. 455-458
Keywords [en]
Cast Iron, Microsegregation, Electron microprobe analysis
National Category
Metallurgy and Metallic Materials
Identifiers
URN: urn:nbn:se:hj:diva-35531ISBN: 978-1-908549-29-7 (print)OAI: oai:DiVA.org:hj-35531DiVA, id: diva2:1095918
Conference
6th Decennial International Conference on Solidification Processing, 25th-28th July 2017, Beaumont Estate, Old Windsor, UK
Note

Included in thesis in manuscript form.

Available from: 2017-05-16 Created: 2017-05-16 Last updated: 2019-05-13Bibliographically approved
In thesis
1. On the solidification of compacted and spheroidal graphite irons
Open this publication in new window or tab >>On the solidification of compacted and spheroidal graphite irons
2017 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

A good understanding of the solidification process of a cast material is essential to understand how the combination of alloy composition and the casting process variables combines into the solid cast component and its performance. The wrong combination may result in poor performance or casting defects. Spheroidal graphite has been well researched in ductile irons (SGI) where it is predominant. Spheroidal graphite is also present in smaller amounts in compacted graphite irons (CGI), but its nature and role in this material is less understood. Recent associations of spheroidal graphite in CGI with shrinkage porosity problems highlights the need for better understanding in this area. The importance of the dendritic austenite structure to the properties and solidification behaviour of cast irons has been highlighted in recent research. However, progress is to a degree limited by lack of practical means to characterize the structure.

In the present work, the transition of a cast iron from SGI to CGI though remelting was studied. As the fraction of SG dropped, the tips of the compacted graphite tended to lose contact with the melt at a later stage. After this occurred, solidification appeared to be dominated by spheroidal graphite. Compacted and spheroidal graphite was found to solidify mostly segregated, and the increased recallescence induced by a higher fraction of compacted graphite displayed small influence on the size distribution of spheroidal graphite apart from the total number and fraction. The partitioning of Si, Mn and Cu in SGI and CGI was found to agree well with each other, as well as with theoretical predictions under the assumptions of zero diffusion of the elements in the solid. This shows that the proportions of spheroidal and compacted graphite has small or no influence on the evolution of these elements in the melt during solidification. A method for characterization of the dendritic austenite in quenched cast irons was introduced and evaluated. The method includes a technique for producing a visual contrast between the ledeburite matrix and the dendritic austenite, and a scheme for producing binary images from the resulting micrographs which are suitable for automatic image analysis. Measurements of the volume fraction and surface area per unit volume of the dendritic austenite structure using the introduced method was found to agree reasonably with traditional point counting and line intercept techniques. The difficulty in finding the exact boundary was proposed to be the major source of systematic disagreement.

Abstract [sv]

En god förståelse för stelningsprocessen av ett gjutet material är väsentligt för att förstå hur kombinationen av legeringens kemiska sammansättning och gjutprocessens variabler resulterar i den stelnade komponenten och dess prestanda. Fel kombination kan resultera i sänkt prestanda eller gjutdefekter. Sfärisk grafit är väl studerad i segjärn (SGI) där grafitmorfologin är dominant. Mindre mängder sfärisk grafit är dock närvarande även i kompaktgrafit, där dess karaktär och roll är mindre känd. Samband mellan sfärisk grafit i kompaktgrafitjärn och krympporositet understryker behovet av bättre förståelse inom detta område. Dessutom har betydelsen av den tidiga dendritiska austenitstrukturen för senare delen av stelningen uppmärksammats. Utveckling inom detta område är dessvärre till en grad begränsad av bristen på kunskap om praktiska metoder för att karaktärisera dess struktur.

I detta arbete studerades övergången från segjärn till kompaktgrafit genom omsmältning. Vid sänkt fraktion sfärisk grafit visade sig kompaktgrafiten tappa kontakten med smältan vid senare stadie av stelningen. Efter detta inträffade, dominerades stelningen till synes av tillväxt av sfärisk grafit. Kompaktgrafit och sfärisk grafit bildades i huvudsak segregerade. Ökad rekallesens till följd av ökad fraktion kompaktgrafit visade sig ha låg inverkan på storleksfördelningen av eutektisk sfärisk grafit bortsett från dess totala antal och fraktion. Omfördelningen av Si, Mn och Cu mellan stelnad matris och smälta i segjärn och kompaktgrafitjärn fanns stämma bra överens med varandra, samt med teoretiska värden med antagande om försumbar diffusion i stelnad matris. Detta visar att proportionerna av sfärisk och kompaktgrafit har liten eller ingen inverkan på halten av dessa ämnen i smältan under stelningen. En metod för karaktärisering av den dendritiska austenitstrukturen i släckt gjutjärn introducerades och utvärderades. Metoden inkluderar en teknik för att åstadkomma kontrast mellan ledeburitmatrisen och den dendritiska austeniten, och en teknik för att producera binära bilder från resulterande mikroskopbilder som är lämpliga för automatisk bildanalys. Mätningar av volymfraktion och yta per volymenhet av dendritstrukturen genom tillämpning av den introducerade metoden visade rimlig överensstämmelse med traditionella punktfraktion‐ och linjetekniker. Svårigheten att hitta den exakta gränslinjen mellan dendritisk struktur och ledeburit föreslogs vara den huvudsakliga källan till systematisk oöverensstämmelse.

Place, publisher, year, edition, pages
Jönköping: Jönköping University, School of Engineering, 2017. p. 48
Series
JTH research report, ISSN 1404-0018 ; 24
Keywords
Compacted graphite iron, Spheroidal graphite iron, Solidification, Microsegregation, Kompaktgrafitjärn, segjärn, stelning, mikrosegregation
National Category
Metallurgy and Metallic Materials
Identifiers
urn:nbn:se:hj:diva-35533 (URN)9789187289255 (ISBN)
Supervisors
Available from: 2017-05-16 Created: 2017-05-16 Last updated: 2017-05-16Bibliographically approved
2. Compacted graphite iron: On solidification phenomena related to shrinkage defects
Open this publication in new window or tab >>Compacted graphite iron: On solidification phenomena related to shrinkage defects
2019 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

An improved understanding of solidification of compacted graphite iron (CGI) is necessary to predict shrinkage related casting defects. Spheroidal graphite is not only found in ductile iron (SGI) but usually also in CGI, but its characteristics and role in this material is less understood. Uncertainties also remain regarding the segregation of alloying elements in cast irons. This is important because of its important role in the solidification process. The dendritic austenite structure has received little attention in cast iron research. A good understanding of the development of this structure is important to understand feeding of melt through the solidifying material.

Nodularity is a measure of the amount of spheroidal versus compacted graphite in the microstructure. At a lower nodularity, the compacted graphite tips were found to grow in contact with the melt for a longer time before being encapsulated in the austenite. Moreover, as the nodularity was reduced, the subpopulation of larger spheroidal graphite gradually disappeared, reducing the bimodal size distribution to unimodal.

Segregation of Si, Mn and Cu in SGI and CGI with a solidification time of near 10 min was found to be rather predictable under assumptions of no diffusion in austenite and complete mixing in the melt. Gradients of these elements contribute to a decrease in the driving force for diffusion of carbon into the austenite from the liquid, which is important for the growth of graphite which is separated from the liquid by austenite.

During solidification of a near-eutectic CGI, the carbon concentration of austenite was found to deviate considerably from local equilibrium with graphite during solidification. This is important to consider in growth models for graphite by diffusion of carbon through a barrier of austenite.

Micropores were shown to have displaced liquid from the solid structure at a late stage of solidification when solidification was slowing down and the temperature of the casting was falling at an increasing rate.

The development of dendritic austenite in a near eutectic CGI was investigated. The contact area between liquid and the dendritic structure exceeded the contact area between liquid and eutectic cells through the dominant part of solidification. This highlights the importance of good understanding of the development of this structure in order to predict feeding of melt through the solidifying material. The coarsening of the structure was found to proceed at a higher rate compared to studies under isothermal condition. The dendritic structure continued to grow in parallel with the eutectic by a combination of thickening and dendritic growth.

Abstract [sv]

En förbättrad förståelse av stelningsförloppet hos kompaktgrafitjärn (CGI) är nödvändig för att förutbestämma krymprelaterade gjutdefekter. Nodulär grafit förekommer inte bara i segjärn (SGI) utan vanligtvis även i CGI, men dess karaktär och roll är mindre känd för detta material. Osäkerheter kvarstår även kring segring av legeringsämnen i gjutjärn, vilket spelar en viktig roll under dess stelningsförlopp. Dendritisk austenitstruktur har fått relativt lite uppmärksamhet bland forskare inom gjutjärn. God kunskap om dess utveckling är viktigt för att förstå matning av smälta genom stelningsförloppet.

Nodularitet är ett mått på andelen nodulär kontra kompakt grafitmorfologi i mikrostrukturen. Vid lägre nodularitet visades kompaktgrafitens extremiter växa i kontakt med smältan en längre period innan de inneslöts av austenit. Gruppen av större nodular försvann dessutom gradvis vid lägre nodularitet, vilket reducerade den starkt bimodala storleksfördelningen till unimodal.

Segring av Si, Mn och Cu i SGI och CGI med stelningstid på nära 10 min fanns förutbestämbar under antaganden om obetydlig diffusion i austenit och omedelbar blandning med smältan. Gradienter av dessa element bidrar till en sänkt drivkraft för diffusion av kol mot austenitens inre, vilket är viktigt för tillväxt av nodulär grafit.

Under stelning av ett nära eutektiskt CGI fanns kolhalten i austenit avvika avsevärt från lokal jämvikt med grafit under stelningen. Detta är viktigt att ta hänsyn till i modeller för tillväxt av grafit genom diffusion av kol genom en barriär av austenit.

En studie av mikroporer visade att dessa trängt undan smälta mellan stelnad struktur i ett sent stadie av stelningen, med avtagande stelningshastighet och ökande temperaturfall.

Utvecklingen av dendritstruktur i ett nära eutektiskt kompaktgrafitjärn undersöktes. Smältans kontaktyta mot denna struktur överskred kontaktyta mot eutektiska stelningskroppar genom större delen av stelningen. Detta visar att en god förståelse för dendritstrukturens utveckling genom stelningen är viktig för att beskriva matning av smälta genom stelnande struktur. Förgrovning av strukturen visades fortskrida i högre takt genom stelningen jämfört med studier vid isotermiskt tillstånd. Dendritstrukturen fortsatte växa parallellt med eutektisk stelning genom en kombination av homoepitaxial och dendritisk tillväxt.

Place, publisher, year, edition, pages
Jönköping: Jönköping University, School of Engineering, 2019. p. 69
Series
JTH Dissertation Series ; 046
Keywords
Compacted graphite iron, Spheroidal graphite iron, Solidification, Microsegregation, Porosity, Kompaktgrafitjärn, segjärn, stelning, mikrosegregation, porositet
National Category
Metallurgy and Metallic Materials
Identifiers
urn:nbn:se:hj:diva-43661 (URN)978-91-87289-49-1 (ISBN)
Public defence
2019-06-12, E1405, School of Engineering, Jönköping, 10:00 (English)
Opponent
Supervisors
Available from: 2019-05-13 Created: 2019-05-13 Last updated: 2019-05-22Bibliographically approved

Open Access in DiVA

Fulltext(895 kB)38 downloads
File information
File name FULLTEXT01.pdfFile size 895 kBChecksum SHA-512
d453bd3f78d4d4e49e178f060820f78109a292a9925d0388981a34841c62c4f5d4ec293b6803c2f3796f8a5753457554129cab2a40e05d9d3c2ae5ef65358ebf
Type fulltextMimetype application/pdf

Authority records BETA

Domeij, BjörnDiószegi, Attila

Search in DiVA

By author/editor
Domeij, BjörnDiószegi, Attila
By organisation
JTH, Materials and Manufacturing
Metallurgy and Metallic Materials

Search outside of DiVA

GoogleGoogle Scholar
Total: 38 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

isbn
urn-nbn

Altmetric score

isbn
urn-nbn
Total: 417 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf