Development of Ultrahigh Strength TRIP Steel Containing High Volume Fraction of Martensite and Study of the Microstructure and Tensile BehaviorVisa övriga samt affilieringar
2018 (Engelska)Ingår i: Transactions of the Indian Institute of Metals, ISSN 0972-2815, E-ISSN 0975-1645, Vol. 71, nr 6, s. 1360-1367Artikel i tidskrift (Refereegranskat) Published
Abstract [en]
A new transformation induced plasticity (TRIP) steel containing high volume fraction of martensite was produced by austempering heat treatment cycle. Microstructure and tensile properties of this TRIP steel were investigated and compared to those of a dual phase (DP) steel with high martensite volume fraction. Microstructural analysis showed a mixture of ferrite, bainite, retained austenite and about 25–30 vol% of martensite in the TRIP steel. As a result of the strain induced transformation of retained austenite to martensite, the TRIP steel showed a strength elongation balance of 86% higher than that for the DP steel. In comparison to the commercial TRIP780 steel, the current TRIP steel showed a 15% higher ultimate tensile strength value while maintaining the same level of ductility. TRIP steel also had a larger work hardening exponent than DP steel at all strains.
Ort, förlag, år, upplaga, sidor
Springer, 2018. Vol. 71, nr 6, s. 1360-1367
Nyckelord [en]
DP steel, Martensite, Retained austenite, TRIP steel, Work hardening
Nationell ämneskategori
Metallurgi och metalliska material
Identifikatorer
URN: urn:nbn:se:hj:diva-38749DOI: 10.1007/s12666-017-1271-yISI: 000431566800008Scopus ID: 2-s2.0-85040740460Lokalt ID: JTHMaterialISOAI: oai:DiVA.org:hj-38749DiVA, id: diva2:1180696
2018-02-062018-02-062019-02-14Bibliografiskt granskad