On the solidification of compacted and spheroidal graphite irons
Högskolan i Jönköping, Tekniska Högskolan, JTH, Material och tillverkning.ORCID-id: 0000-0001-6938-037X
2017 (Engelska)Licentiatavhandling, sammanläggning (Övrigt vetenskapligt)
Abstract [en]

A good understanding of the solidification process of a cast material is essential to understand how the combination of alloy composition and the casting process variables combines into the solid cast component and its performance. The wrong combination may result in poor performance or casting defects. Spheroidal graphite has been well researched in ductile irons (SGI) where it is predominant. Spheroidal graphite is also present in smaller amounts in compacted graphite irons (CGI), but its nature and role in this material is less understood. Recent associations of spheroidal graphite in CGI with shrinkage porosity problems highlights the need for better understanding in this area. The importance of the dendritic austenite structure to the properties and solidification behaviour of cast irons has been highlighted in recent research. However, progress is to a degree limited by lack of practical means to characterize the structure.

In the present work, the transition of a cast iron from SGI to CGI though remelting was studied. As the fraction of SG dropped, the tips of the compacted graphite tended to lose contact with the melt at a later stage. After this occurred, solidification appeared to be dominated by spheroidal graphite. Compacted and spheroidal graphite was found to solidify mostly segregated, and the increased recallescence induced by a higher fraction of compacted graphite displayed small influence on the size distribution of spheroidal graphite apart from the total number and fraction. The partitioning of Si, Mn and Cu in SGI and CGI was found to agree well with each other, as well as with theoretical predictions under the assumptions of zero diffusion of the elements in the solid. This shows that the proportions of spheroidal and compacted graphite has small or no influence on the evolution of these elements in the melt during solidification. A method for characterization of the dendritic austenite in quenched cast irons was introduced and evaluated. The method includes a technique for producing a visual contrast between the ledeburite matrix and the dendritic austenite, and a scheme for producing binary images from the resulting micrographs which are suitable for automatic image analysis. Measurements of the volume fraction and surface area per unit volume of the dendritic austenite structure using the introduced method was found to agree reasonably with traditional point counting and line intercept techniques. The difficulty in finding the exact boundary was proposed to be the major source of systematic disagreement.

Abstract [sv]

En god förståelse för stelningsprocessen av ett gjutet material är väsentligt för att förstå hur kombinationen av legeringens kemiska sammansättning och gjutprocessens variabler resulterar i den stelnade komponenten och dess prestanda. Fel kombination kan resultera i sänkt prestanda eller gjutdefekter. Sfärisk grafit är väl studerad i segjärn (SGI) där grafitmorfologin är dominant. Mindre mängder sfärisk grafit är dock närvarande även i kompaktgrafit, där dess karaktär och roll är mindre känd. Samband mellan sfärisk grafit i kompaktgrafitjärn och krympporositet understryker behovet av bättre förståelse inom detta område. Dessutom har betydelsen av den tidiga dendritiska austenitstrukturen för senare delen av stelningen uppmärksammats. Utveckling inom detta område är dessvärre till en grad begränsad av bristen på kunskap om praktiska metoder för att karaktärisera dess struktur.

I detta arbete studerades övergången från segjärn till kompaktgrafit genom omsmältning. Vid sänkt fraktion sfärisk grafit visade sig kompaktgrafiten tappa kontakten med smältan vid senare stadie av stelningen. Efter detta inträffade, dominerades stelningen till synes av tillväxt av sfärisk grafit. Kompaktgrafit och sfärisk grafit bildades i huvudsak segregerade. Ökad rekallesens till följd av ökad fraktion kompaktgrafit visade sig ha låg inverkan på storleksfördelningen av eutektisk sfärisk grafit bortsett från dess totala antal och fraktion. Omfördelningen av Si, Mn och Cu mellan stelnad matris och smälta i segjärn och kompaktgrafitjärn fanns stämma bra överens med varandra, samt med teoretiska värden med antagande om försumbar diffusion i stelnad matris. Detta visar att proportionerna av sfärisk och kompaktgrafit har liten eller ingen inverkan på halten av dessa ämnen i smältan under stelningen. En metod för karaktärisering av den dendritiska austenitstrukturen i släckt gjutjärn introducerades och utvärderades. Metoden inkluderar en teknik för att åstadkomma kontrast mellan ledeburitmatrisen och den dendritiska austeniten, och en teknik för att producera binära bilder från resulterande mikroskopbilder som är lämpliga för automatisk bildanalys. Mätningar av volymfraktion och yta per volymenhet av dendritstrukturen genom tillämpning av den introducerade metoden visade rimlig överensstämmelse med traditionella punktfraktion‐ och linjetekniker. Svårigheten att hitta den exakta gränslinjen mellan dendritisk struktur och ledeburit föreslogs vara den huvudsakliga källan till systematisk oöverensstämmelse.

Ort, förlag, år, upplaga, sidor
Jönköping: Jönköping University, School of Engineering , 2017. , s. 48
Serie
JTH research report, ISSN 1404-0018 ; 24
Nyckelord [en]
Compacted graphite iron, Spheroidal graphite iron, Solidification, Microsegregation
Nyckelord [sv]
Kompaktgrafitjärn, segjärn, stelning, mikrosegregation
Nationell ämneskategori
Metallurgi och metalliska material
Identifikatorer
URN: urn:nbn:se:hj:diva-35533ISBN: 9789187289255 (tryckt)OAI: oai:DiVA.org:hj-35533DiVA, id: diva2:1095932
Handledare
Tillgänglig från: 2017-05-16 Skapad: 2017-05-16 Senast uppdaterad: 2017-05-16Bibliografiskt granskad
Delarbeten
1. Size distribution of graphite nodules in hypereutectic cast irons of varying nodularity
Öppna denna publikation i ny flik eller fönster >>Size distribution of graphite nodules in hypereutectic cast irons of varying nodularity
2018 (Engelska)Ingår i: Metallurgical and materials transactions. B, process metallurgy and materials processing science, ISSN 1073-5615, E-ISSN 1543-1916, Vol. 49, nr 5, s. 2487-2504Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

An SGI was machined into 400 g cylindrical pieces and remelted in an electrical resistance furnace protected by Ar gas to produce materials ranging from SGI to CGI. The graphite morphology was controlled by varying the holding time at 1723 K (1450 °C) between 10 and 60 minutes. The discrete sectional size distribution of nodules by number density was measured on cross sections of the specimens and translated to volumetric distribution by volume fraction. Subpopulations of nodules were distinguished by fitting Gaussian distribution functions to the measured distribution. Primary and eutectic graphite, were found to account for most of the volume of nodular graphite in all cases. For holding times of 40 minutes and greater, corresponding to nodularity roughly below 40 pct, the primary subpopulation was very small and difficult to distinguish, leaving eutectic nodules as the dominant subpopulation. The mode and standard deviation of the two subpopulations were roughly independent of nodularity. Moreover, the nodular and vermicular graphite were segregated in the microstructure. In conclusion, the results suggest that the parallel development of the vermicular eutectic had small influence on the size distribution of eutectic graphite nodules.

Ort, förlag, år, upplaga, sidor
Springer, 2018
Nationell ämneskategori
Metallurgi och metalliska material
Identifikatorer
urn:nbn:se:hj:diva-35530 (URN)10.1007/s11663-018-1274-z (DOI)000444765500033 ()2-s2.0-85048767236 (Scopus ID)HOA JTH 2018 (Lokalt ID)HOA JTH 2018 (Arkivnummer)HOA JTH 2018 (OAI)
Anmärkning

Included in licentiate thesis by Björn Domeij (2017), On the solidification of compacted and spheroidal graphite irons, as manuscript.

Tillgänglig från: 2017-05-16 Skapad: 2017-05-16 Senast uppdaterad: 2019-05-13Bibliografiskt granskad
2. Inferring the development of microsegregation and microstructure in Spheroidal and Compacted Graphite Iron using EPMA‐WDS
Öppna denna publikation i ny flik eller fönster >>Inferring the development of microsegregation and microstructure in Spheroidal and Compacted Graphite Iron using EPMA‐WDS
2017 (Engelska)Ingår i: Solidification Processing 2017: Proceedings of the 6th Decennial International Conference on Solidification Processing / [ed] Zhongyun Fan, Brunel Centre for Advanced Solidification Technology (BCAST) , 2017, nr 1, s. 455-458Konferensbidrag, Publicerat paper (Refereegranskat)
Abstract [en]

Microsegregation is closely related to the solidification characteristics and microstructure development of a material. In this paper, the microsegregation of Si, Cu, Mn, and P was investigated on a spheroidal and a compacted graphite iron using a modified EPMA equipped with WDS spectrometers. On the basis of the approximated local equilibrium eutectic temperature, the solidification sequence of the matrix was estimated. The inferred microstructure development appeared to correspond well to published interrupted solidification experimental results. Solute profiles and effective partition coefficients were constructed using the solidification sequence. While the spatial microsegregation patterns clearly differed between the two materials, solute profiles and effective partition coefficients were very similar. For Si, Cu and Mn, the solute profiles corresponded reasonably with simulation results produced using the Scheil-Gulliver module of the Thermo-Calc software with the TCFE7 databank, indicating back-diffusion of these elements is negligible for SGI and CGI with solidification times up to 10 min. The effective partition coefficients for Si, Cu and Mn were fairly constant until about 90% of the matrix had solidified, after which they appeared to approach unity.

Ort, förlag, år, upplaga, sidor
Brunel Centre for Advanced Solidification Technology (BCAST), 2017
Nyckelord
Cast Iron, Microsegregation, Electron microprobe analysis
Nationell ämneskategori
Metallurgi och metalliska material
Identifikatorer
urn:nbn:se:hj:diva-35531 (URN)978-1-908549-29-7 (ISBN)
Konferens
6th Decennial International Conference on Solidification Processing, 25th-28th July 2017, Beaumont Estate, Old Windsor, UK
Anmärkning

Included in thesis in manuscript form.

Tillgänglig från: 2017-05-16 Skapad: 2017-05-16 Senast uppdaterad: 2019-05-13Bibliografiskt granskad
3. Quantification of dendritic austenite after interrupted solidification in a hypoeutectic lamellar graphite iron
Öppna denna publikation i ny flik eller fönster >>Quantification of dendritic austenite after interrupted solidification in a hypoeutectic lamellar graphite iron
2016 (Engelska)Ingår i: Metallography, Microstructure, and Analysis, ISSN 2192-9270, Vol. 5, nr 1, s. 28-42Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

This paper presents an unconventional etching technique to reveal the microstructure in a hypoeutectic lamellar graphite iron that has been quenched after isothermal heat treatment in the proeutectic semi-solid temperature region. A technique for quantifying the dendrite microstructure using the aforementioned etching technique involving a combination of a raster graphics editor and an image analysis software is outlined. The agreement between this quantification technique with regard to volume fraction and surface area per unit volume of the dendritic austenite and corresponding point counting and line intercept techniques is analyzed. The etching technique was found useful but sporadic tinting of martensite was problematic. Some measurements showed significant systematic disagreement which correlated with the coarseness of the measured dendrites. Most systematic disagreement is attributed to difficulties in defining the dendrite boundary in the analogues and much of the random disagreement to easily identified discrepancies between the analogue and the micrograph.

Ort, förlag, år, upplaga, sidor
New York: Springer, 2016
Nyckelord
Cast iron, Quantitative metallography, Color metallography, Microstructure
Nationell ämneskategori
Metallurgi och metalliska material
Identifikatorer
urn:nbn:se:hj:diva-28880 (URN)10.1007/s13632-015-0250-0 (DOI)000377604200007 ()2-s2.0-84960404906 (Scopus ID)
Projekt
Spofic II
Forskningsfinansiär
VINNOVA, 2013-04720
Anmärkning

One of five papers selected for the 2016 Editor’s Choice.

Tillgänglig från: 2016-01-07 Skapad: 2016-01-07 Senast uppdaterad: 2019-05-13Bibliografiskt granskad

Open Access i DiVA

Kappa(7634 kB)560 nedladdningar
Filinformation
Filnamn FULLTEXT01.pdfFilstorlek 7634 kBChecksumma SHA-512
211bdf79ffc913a92abdec7a99228f63f4256435e6d7c8906295e8e0cf40deaad0071fb4f3f92d228619e30116592c907205fb7602da149615128c2747457752
Typ fulltextMimetyp application/pdf

Personposter BETA

Domeij, Björn

Sök vidare i DiVA

Av författaren/redaktören
Domeij, Björn
Av organisationen
JTH, Material och tillverkning
Metallurgi och metalliska material

Sök vidare utanför DiVA

GoogleGoogle Scholar
Totalt: 560 nedladdningar
Antalet nedladdningar är summan av nedladdningar för alla fulltexter. Det kan inkludera t.ex tidigare versioner som nu inte längre är tillgängliga.

isbn
urn-nbn

Altmetricpoäng

isbn
urn-nbn
Totalt: 1286 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf