The effect of SI content on microstructure and mechanical properties of Al-Si alloy
Högskolan i Jönköping, Tekniska Högskolan, JTH, Material och tillverkning.ORCID-id: 0000-0001-5753-4052
Högskolan i Jönköping, Tekniska Högskolan, JTH. Forskningsmiljö Material och tillverkning – Gjutning.ORCID-id: 0000-0001-6481-5530
Högskolan i Jönköping, Tekniska Högskolan, JTH. Forskningsmiljö Material och tillverkning – Gjutning.
2016 (engelsk)Inngår i: La Metallurgia Italiana, ISSN 0026-0843, Vol. 108, nr 6Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]

Al-Si alloys are the most popular casting alloys due to their excellent castability combined with high strengthto-weight ratio. This paper investigates the role of Si content in the range of 6.5 wt. % to 14.4 wt. % on the microstructure and mechanical properties of Al-Si-Mg casting alloys. All alloys were modified with 90-150 ppm Sr. No grain refiner was added. The samples were produced by directional solidification providing a microstructure that corresponds to microstructures found in die castings. From the phase diagram and coupled zone, increasing the Si level up to 14.4 wt. % is expected to start a competition between formation of α- dendrites and a fully eutectic microstructure. However, it is known that Sr-modification shifts the eutectic to higher Si contents. For the lower Si contents, the microstructure of the samples consisted of α-dendrites and a modified Al-Si eutectic. At 12.4 wt. % Si and above, a cellular eutectic microstructure was observed. No primary Si was observed even at 14.4 wt. % Si. The mechanical properties in terms of yield and tensile strength did not vary remarkably as a function of the Si level unlike the elongation to failure that dropped from 12 % at 6.5 wt. % Si to nearly 6 % at 14.4 wt. % Si; but still the material is exhibiting an elongation to failure that is far higher than normally expected.

sted, utgiver, år, opplag, sider
Milano: Associazione Italiana di Metallurgia , 2016. Vol. 108, nr 6
Emneord [en]
Al-Si alloy, Fracture mechanism, Mechanical Properties, Dendritic eutectic growth, Microstructure
HSV kategori
Identifikatorer
URN: urn:nbn:se:hj:diva-31156Scopus ID: 2-s2.0-85008867852OAI: oai:DiVA.org:hj-31156DiVA, id: diva2:950725
Tilgjengelig fra: 2016-08-02 Laget: 2016-08-02 Sist oppdatert: 2017-11-28bibliografisk kontrollert

Open Access i DiVA

fulltext(320 kB)177 nedlastinger
Filinformasjon
Fil FULLTEXT01.pdfFilstørrelse 320 kBChecksum SHA-512
452bc836a5626b170a3bd9b570109adbe5b8cd5c79e735ef3ca44b8efae0bc1c37ef1f77d58499ba3fef960330992c26f27729f82eceac0a5119c4ffb083d358
Type fulltextMimetype application/pdf

Scopus

Personposter BETA

Bogdanoff, ToniSeifeddine, SalemDahle, Arne K.

Søk i DiVA

Av forfatter/redaktør
Bogdanoff, ToniSeifeddine, SalemDahle, Arne K.
Av organisasjonen
I samme tidsskrift
La Metallurgia Italiana

Søk utenfor DiVA

GoogleGoogle Scholar
Totalt: 177 nedlastinger
Antall nedlastinger er summen av alle nedlastinger av alle fulltekster. Det kan for eksempel være tidligere versjoner som er ikke lenger tilgjengelige

urn-nbn

Altmetric

urn-nbn
Totalt: 735 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf